2310 Oily Synthetic Fiber Paint Silk Introduction

Product name: oil synthetic fiber paint silk

Model: 2310

Main composition: polyester silk, oil paint

Features and USES: high electrical, mechanical properties suitable for the insulation of packing and gasket in electrical appliances

Heat resistance grade: grade A

Execution standard: JB/T 7772-1995

Thickness: 0.08, 0.10, 0.12, 0.15, 0.17mm;

Width:15, 20, 25mm.

2310 Oily Synthetic Fiber Paint Silk Technical parameters

Model Nominal thickness
and tolerance
Minimum Tensile Strength (N / 10mm) Width Elasticity Breakdown voltage (KV) min
Lengthwise Crosswise 45°
direction
Tension elongation 6%(N) 23±2℃ 23±2℃
After bending
105±2℃ After heating &bending 24hHumidity after 24h 6%Elongate 6% on 45° degree
mid min mid min mid min mid  Max Mid Min Mid Min Mid Min Mid Min Mid Min Mid Min
2210/
2310
0.04±0.010 10 7 7 5 7 5
0.05±0.010 14 9 9 7 9 7 /1-9 /11
0.06±0.010 18 11 11 9 11 9 /2-10 /12
0.08±0.010 22 16 15 10 15 10 2-10
1-8
11/
10
4.8 2.4 3.0 1.8 3.0 1.8 2.5 1.4 2.3 1.4 2.7
0.10±0.010 24 18 17 12 17 12 2-12
1-9
1-9
14/
11
5.8 3.8 4.4 2.2 4.3 2.2 3.7 1.7 3.5 2.0 4.1 2.1
0.12±0.010 25 20 18 14 18 14 3-12
1-10
14/
12
7.2 4.8 6.3 3.2 5.2 2.5 4.0 2.1 4.1 2.5 5.0 2.5
0.15
±0.010
30 24 22 18 22 18 3-14
1-14
17/
17
8.7 5.2 6.9 3.8 5.8 3.1 4.2 2.7 4.7 2.8 6.1 3.1
Thermoplasticity After 24h on 70±2℃, varnished silk must not bond interlayer or come off from the bottom
Influence of oil on Varnished silk 2212 required: After 18h in 45 transformer oil on 105±2℃ , varnished silk can’t bond interlayer, the film can not fall off
Shrinkage Heating under 105±2℃, Thermal Shrinkage of 2210≤1%, Thermal Shrinkage of 2310≤ 4%
Volume resistivity 23±2℃ ≥1.0×1011 105±2℃ ≥1.0×108 Humidity after 24h ≥1.0×108