2210 Oil Varnished/coated Synthetic Fabric

1. Peoduction description 
1. Heat resistance class:H
2. Raw material: 2210 Oil Varnished/coated Synthetic Fabric is made from silk and oil paint 
3.Application: It has good electrical and mechanical performances, it will be used at 105 centigrade or l
 

E-mail:yolo@ztaero.com

 


Overview:

1. Heat resistance class:H 2. Raw material: 2210 Oil Varnished/coated Synthetic Fabric is made from silk and oil paint 3.Application: It has good electrical and mechanical performances, it will be used at 105 centigrade or less for a long period. It can be used for the binding and insulating materials for the electric motor, appliance, etc. 4.Standard: According to JB/T 8147-1999 standard.

Technical parameters

Model and tolerance      
    Lengthwise Crosswise 45° direction     23±2℃ After bending   After heating &bending    
    mid min mid min mid min mid Max Mid Min Mid Min Mid Min Mid Min Mid Min Mid Min
2210/ 0.04±0.010 10 7 7 5 7 5                            
2310 0.05±0.010 14 9 9 7 9 7 /1-9 /11                        
  0.06±0.010 18 11 11 9 11 9 /2-10 /12                        
  0.08±0.010 22 16 15 10 15 10 /2/10 11/ 4.8 2.4 3 1.8 3 1.8 2.5 1.4 2.3 1.4 2.7  
  1/8 10
  0.10±0.010 24 18 17 12 17 12 2/12 14/ 5.8 3.8 4.4 2.2 4.3 2.2 3.7 1.7 3.5 2 4.1 2.1
    11
  1/9  
  0.12±0.010 25 20 18 14 18 14 3/12 14/ 7.2 4.8 6.3 3.2 5.2 2.5 4 2.1 4.1 2.5 5 2.5
  1/10 12
  0.15 30 24 22 18 22 18 3/14 17/ 8.7 5.2 6.9 3.8 5.8 3.1 4.2 2.7 4.7 2.8 6.1 3.1
  ±0.010 1/14 17
Thermoplasticity After 24h on 70±2℃, varnished silk must not bond interlayer or come off from the bottom
Influence of oil on Varnished silk 2212 required: After 18h in 45 transformer oil on 105±2℃ , varnished silk can’t bond interlayer, the film can not fall off
Shrinkage 4%Heating under 105±2℃, Thermal Shrinkage of 2210≤1%, Thermal Shrinkage of 2310≤ 4%
Volume resistivity Under 23±2℃ ≥1.0×1011 Under 105±2℃ ≥1.0×108 Humidity after 24h ≥1.0×108